| 摘要: |
| 对TiB2金属陶瓷与TiAl金属间化合物进行了扩散连接试验,研究了直接扩散连接和采用Ni为中间层进行扩散连接的接头界面结构及工艺参数对界面结构和连接性能的影响。直接扩散连接时,连接界面处生成了Ti(Cu,Al)2金属间化合物,采用Ni为中间层进行扩散连接时,界面处生成了单层TiAlNi2金属间化合物层和两层Ti,Al,Ni扩散层共三层结构。直接扩散连接时,连接温度T=1223K,时间t=1.8ks,压力p=80MPa时接头强度为103MPa;采用Ni为中间层时,连接温度T=1273K,时间t=1.8ks,压力p=80MPa时接头强度为110MPa。 |
| 关键词: TiB2金属陶瓷 TiAl 扩散连接 界面结构 |
| DOI： |
| 分类号: |
| 基金项目:国家自然科学基金资助项目(50175021) |
|
| Diffusion bonding of TiB2 cermet to TiAl intermetallic |
|
LI Zhuo ran, CAO Jian, FENG Ji cai
|
|
National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China
|
| Abstract: |
| The diffusion bonding of TiB2 cermet to TiAl intermetallic was studied in this paper.The effects of bonding parameters on the microstructure of the joints and mechanical properties was investigated.The results showed that a Ti (Cu,Al)2 intermetallic layer was formed at the interface between TiB2 cermet and TiAl intermetallic when directly diffusion bonding.A TiAlNi2 intermetallic layer and two Ti,Al,Ni solid solution layers were formed at the interface by using Ni interlayer.The shear strength was 103 MPa when directly diffusion bonding with bonding temperature T=1 223 K,bonding time t=1.8 ks and bonding pressure p=80 MPa,and the shear strength was 110 MPa by using Ni layer with T=1 223 K,t=1.8 ks and p=80 MPa. |
| Key words: TiB2 cermet TiAl intermetallic diffusion bonding interface microstructure |