| 摘要: |
| 依据BS7448断裂韧度试验标准(ISO/TC164/SC4-N400),对采用埋弧焊(SAW)工艺施焊的、板厚为54 mm的海洋石油平台大厚度对接接头试样进行了低温裂纹尖端张开位移(CTOD)试验。分别测试了-15℃下单丝和双丝埋弧焊工艺下焊缝金属和热影响区的CTOD值。试验表明,除双丝埋弧焊热影响区试件外,其余试件均满足挪威船级社DNV规定的最小特征CTOD为0.15 mm的要求,为指导海洋平台的施工建造提供了科学依据。 |
| 关键词: 单丝埋弧焊 双丝埋弧焊 裂纹尖端张开位移 断裂韧度 |
| DOI： |
| 分类号: |
| 基金项目:国家自然科学基金资助项目(50375109);中国海洋石油工程股份有限公司资助项目 |
|
| Fracture toughness for large welded joints in offshore platform |
|
ZUO Bo1, ZHANG Yu-feng1, HUO Li-xing1, BAI Bing-ren2, LI Xiao-wei2, CHAO Jun2
|
|
1.Tianjin University, Tianjin 300072, China;2.Offshore Petroleum Engineering Company, Tianjin 300452, China
|
| Abstract: |
| The measuring and testing technique of crack tip opening displacement (CTOD)tests for large welded joints in the offshore platformunder low environmental temperatures of -15℃ were performed in accordance with the BS 7448 standard(part2, 1997).The CTOD tests on the weld metal and heat affected zone were conducted for the welded jointswith a thickness of 54 mm welded by single electrode and twin electrode of submerged-arc welding technology respectively .The testing results provide judgements on whether the joints need postweld heat treatment. |
| Key words: single electrode submerged arc welding twin electrode submeraged welding crack tip opening displacement fracture toughness |