| 根据Si3N4陶瓷钎焊性和非晶形成能力的要求,确定非晶钎料合金成分为Ti40Zr25Ni15Cu20;采用单辊熔体快淬法成功制备了箔带状Ti40Zr25Ni15Cu20钎料合金,并通过X射线衍射、差热分析、电镜线扫描等分析手段证实其为非晶态。试验结果表明,Ti40Zr25N i15Cu20合金其约化玻璃温度Trg=0.76,过冷液相区ΔTx=78K。 |
| 关键词: Si3N4陶瓷 活性钎料 非晶态 Ti-Zr-Ni-Cu |
| DOI： |
| 分类号: |
| 基金项目:江苏省自然科学基金资助项目(BK2003045);江苏省高校自然科学基金资助项目(03KJB3006);江苏省高校省级重点实验室开放研究基金项目 |
|
| Research of Ti-Zr-Ni-Cu based amorphous brazing material |
|
ZOU Jia-sheng1,2, XU Zhi-rong2, JIANG Zhi-guo2, ZHAO Qi-zhang2
|
|
1.Department of Materials Science and Engineering, Nanjing University of Science and Technology, Jiangsu Nanjing 210094, China;2.Province Key Lab of Advanced Welding Technology, Jiangsu University of Science and Technology, Jiangsu Zhenjiang 212003, China
|
| Abstract: |
| According to the brazing properties of Si3N4 ceramic and the requirement for GFA,a new kind of amorphous alloy composition of Ti40Zr25Ni15Cu20 was proposed.Amorphous ribbon samples of Ti40Zr25Ni15Cu20 alloy were produced by melt spinning in roll forging machine in argon atmosphere.The amorphous structure was examined by X-ray diffractometry and differential thermal analysis(DTA).Alloy composition was measured by EDS.The reduced glass transition temperature(Trg) and the temperature interval of supercooled liquid region before crystallization are 0.76 and 78 K,respectively. |
| Key words: active solder Si3N4 ceramic amorphous TiZr-Ni-Cu |