| Preparation of water-resistant electrode coating with stearic acid by microwave reaction |
|
CHEN Wenjun1, DAI Le2, GUI Chibin3
|
|
1.College of Naval Architecture and Power, Naval University of Engineering, Wuhan 430033, China;2.Military Representative Office of Navy in 407 Factory, Luoyang 471039, China;3.College of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China
|
| Abstract: |
| Absorbing moisture of electrode coating may easily lead to high diffusible hydrogen of weld metal, resulting in hydrogen embrittlement, blowhole, cold crack and other defects. Electrode was immersed to the petroleum ether solution containing stearic and Fe3 O4 powder, after that electrode was treated by the microwave oven and then became water-resistant. Microwave absorption material Fe3 O4 was used to reduce the diffusible hydrogen of weld bead, and promote the reaction of stearic acid and electrode surface. The results of FT-IR and SEM microscope indicate that Fe3 O4 absorbs microwave and melt stearic acid to form the water-resistant film. The diffusible hydrogen of the deposited metal of microwave treated electrode decreased to 70% of the one made by the untreated electrode, and such property does not vary very much as the the stoving time keeping 8 h. |
| Key words: absorbing moisture protecting film electrode microwave stearic acid |