| 摘要: |
| 采用激光熔覆技术在H13热作模具钢表面分别制备了Co50合金涂层和TiC/Co基复合涂层.借助XRD,SEM与显微硬度计对比分析了涂层与基材的结合状态、涂层物相组成、截面组织形貌和显微硬度分布.结果表明,Co50合金涂层和TiC/Co基复合涂层均与H13钢基材呈良好冶金结合特征.Co50合金涂层主要由初生γ-Co枝晶及其间的共晶组织组成,而TiC/Co基复合涂层主要由TiC颗粒、枝晶及细小的共晶组织组成,其组成相除含有TiC,TiCo3和Cr2Ni3外,还有Cr-Ni-Fe-C等相.涂层截面显微硬度分布表明,TiC/Co基复合涂层截面平均显微硬度明显高于Co50合金涂层,分别为5520 MPa和4990 MPa,分别是H13钢基材的2.7和2.4倍. |
| 关键词: 激光熔覆 热作模具钢 钴基合金 复合涂层 |
| DOI： |
| 分类号: |
| 基金项目:国家自然科学基金资助顶目(51261013,51165015) |
|
| Microstructure and mechanical properties of TiC/Co composite coating by laser cladding on H13 steel surface |
|
PHAM THI HONG NGA1,2, ZHANG Xiaowei1, WANG Chuanqi1, LIU Hongxi1, JIANG Yehua1
|
|
1.College of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China;2.College of Mechanical Engineering, University of Technical Education Ho Chi Minh City, Ho Chi Minh 720035, Vietnam
|
| Abstract: |
| TiC/Co composite coating and Co50 alloy coating were prepared by laser cladding of on the AISI H13 hot work tool steel surface.The bonding characteristics,phase constitution, microstructure and micro-hardness distribution of the coatings were analyzed and tested by XRD,SEM and micro-hardness tester.The results indicate that Co50 alloy coating as well as TiC/Co composite coating show good metallurgical bonding with the H13 steel substrate surface.Co50 alloy coating was mainly composed of γ-Co dendrite and eutectic between γ-Co dendrites, while TiC/Co composite coating which contained TiC particles, dendrite and fine eutectic,was consisted of TiC,TiCo3,Cr2Ni3 as well as Cr-Ni-Fe-C,and so on.The average micro-hardness of cross-section of TiC/Co-based composite coating and Co50 alloy coating are 5520 MPa and 4990 MPa,about 2.7 times and 2.4 times higher than that of the H13 steel substrate. |
| Key words: laser cladding AISI H13 steel Co-based alloy composite coating |