| 摘要: |
| 采用Sn-Cu-Ni-xPr无铅钎料对片式电阻进行钎焊试验,并且利用加速老化试验模拟片式电阻中焊点的服役环境,研究了时效过程中Sn-Cu-Ni-xPr焊点界面化合物层的厚度以及焊点抗剪强度的变化.结果表明,随着时效的进行,片式电阻Sn-Cu-Ni-xPr焊点的厚度不断增加,抗剪强度不断下降.与此同时,添加微量稀土元素Pr可有效提高Sn-Cu-Ni-xPr焊点的力学性能,当Pr元素含量为0.05%时,焊点力学性能优良,且在长时间的时效条件下仍然优于其它焊点. |
| 关键词: 无铅钎料 时效 界面厚度 力学性能 |
| DOI： |
| 分类号: |
| 基金项目:中央高校基本科研业务费专项资金资助项目;南京航空航天大学研究生创新基地(实验室)开放基金资助项目(kfjj120122);大学生创新基金资助项目(011231) |
|
| Effect of thermal aging on intermetallic compounds and properties of Sn-Cu-Ni-xPr/Cu soldered joints |
|
MA Chaoli1, XUE Songbai1, LI Yang1, XU Yiwei1, JIANG Junyi2
|
|
1.College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;2.Jinhua Shuanghuan Brazing Alloys Co., Ltd, Jinhua 321000, China
|
| Abstract: |
| Chip resistors were joined with Sn-0.7Cu-0.05Ni-xPr solder. To guarantee the reliability of the Sn-0.7Cu-0.05Ni-xPr/Cu joints in service requirement,the growth rate of intermetallic compounds of Cu side was evaluated and the effects of the intermetallic compound layer on the electrical and mechanical properties have been investigated under various aging time. The shear strength of Sn-0.7Cu-0.05Ni-xPr/Cu joint gradually decreased during thermal aging. Meanwhile,under the same condition, the Sn-0.7Cu-0.05Ni-xPr/Cu joint achieved good mechanical properties when the addition of Pr was about 0.05%. |
| Key words: lead free solder thermal aging interface thickness mechanical properties |